Self-powered stable high-performance UV-Vis-NIR broadband photodetector based on PVP-Cobalt@Carbon nanofibers/n-GaAs heterojunction

The self-powered PVP-Co@C nanofibers/n-GaAs heterojunction photodetector (HJPD) was fabricated by electrospinning of the nanofibers onto GaAs. An excellent rectification ratio of 6.60 x 106 was obtained from I-V measurements of the device in the dark. The I-V measurements of the fabricated device under 365 nm, 395 nm and 850 nm lights, as well as I-V measurements in visible light depending on the light intensity, were performed. The HJPD demonstrated excellent photodetection performance in terms of a good responsivity of similar to 225 mA W-1 (at -1.72 V) and at zero bias, an impressive detectivity of 6.28 x 1012 Jones, and a high on/off ratio of 8.38 x 105, all at 365 nm wavelength. In addition, the maximum external quantum efficiency and NPDR values were 3495% (V = -1.72 V) and 2.60 x 1010 W-1 (V = 0.0 V), respectively, while the minimum NEP value was similar to 10-14 W.Hz-1/2 for 365 nm at V = 0.V volts. The HJPD also exhibited good long-term stability in air after 30 d without any encapsulation.

Dergi

NANOTECHNOLOGY

Yıl

2024

Cilt

35

Sayı

33

ISSN

0957-4484

eISSN

1361-6528

DOI

10.1088/1361-6528/ad4973

WoS UID

WOS:001233330700001