Effect of MGZN2 addition on the sintering density, microstructure and hardness of aluminum alloys prepared by powder metallurgy method

Cardakli, Ismail Seckin, Karadeniz, Sükran, Arslan, Ersin, Gok, Dilsad Akgümüs

Abstract

In this study, the aluminum alloys with different MgZn2 contents were prepared using the powder metallurgy method. The effect of the MgZn2 contents on the sintering density, po-rosity, microstructure and microhardness was investigated using optical microscopy, scan-ning electron microscopy (SEM), X-ray diffraction, and Vickers microhardness. The function mechanism of the intermetallic compounds formed as a result of MgZn2 addition was ana-lyzed. The results revealed that the highest sintering relative density (95.1%), lowest porosity volume fraction (4.81%), and highest hardness (112.4 HV) were observed with the 5% addi-tion of MgZn2 contents. The XRD results show that the microstructure of the bare sample (Al) is mainly composed alpha-Al phase, while, with the addition of MgZn2, the microstructure turned to have alpha-Al phase and some intermetallic compounds of Al5Mg11Zn4 and AlMg4Zn11. These intermetallic compounds were formed with higher density at the grain boundaries as white precipitates.

Keywords

Aluminum Powder Metallurgy Porosity Intermetallic Compounds Sintering Density MECHANICAL-PROPERTIES GRAIN-REFINEMENT MG-ALLOY ZN AL PRECIPITATION

WoS Categories

Engineering, Multidisciplinary

Sustainable Development Goals

Responsible Consumption and Production

Citation

Journal: SIGMA JOURNAL OF ENGINEERING AND NATURAL SCIENCES-SIGMA MUHENDISLIK VE FEN BILIMLERI DERGISI
Year: 2023
Volume: 41
Issue: 3
Pages: 538-544
ISSN: 1304-7205
eISSN: 1304-7191
DOI: 10.14744/sigma.2023.00060
WoS UID: WOS:001009447700001

Open via DOI