Current-voltage-measurement temperature characteristics depending on the barrier-forming contact metal thickness in Au/Cu/<i>n</i>-Si/Au-Sb/Ni rectifying contacts

We experimentally have introduced the current-voltage-temperature (I-V-T) characteristics of the Au/n-type Si (D1), Au/Cu/n-Si (D2), Au/Cu(4 nm)/n-Si (D3) and Au/Cu(2 nm)/n-Si (D4) Schottky-barrier diodes (SBDs) in the temperature range of 40-320 K with the step of 10 K. The copper Schottky contact (SC) dots for the D2, D3 and D4 SBDs have the thickness of 100 nm, 4 nm and 2 nm, respectively. The top Au contact has been used as a shield to prevent oxidation of the copper SC metal. The Schottky barrier height (SBH) Phi(b0) values of 0.61 eV, 0.66 eV and 0.69 eV, and the ideality factor values of 1.04, 1.04 and 1.02 for the D2, D3 and D4 SBDs have been obtained at 300 K, respectively. The SBH value has increased with decreasing Cu thin film thickness. An average series resistance R-s value of 10.6 omega has been obtained for the Au/Cu/n-Si diodes at 300 K. The obtained R-s and the ideality factor values are almost independent of the SC metal thickness. In the SBH vs temperature plots, the SBH value in the D3 and D4 diodes with 2 nm and 4 nm metal thickness almost remained unchanged from 320 K to 120 K, and in the D2 SBD from 320 K to 160 K. Therefore, it can be said from these results that the quality of the SBDs has increased with decrease in Cu Schottky film thickness.

Journal

MATERIALS SCIENCE IN SEMICONDUCTOR PROCESSING

Year

2022

Volume

143

ISSN

1369-8001

eISSN

1873-4081

DOI

10.1016/j.mssp.2022.106532

WoS UID

WOS:000792914200005