Experimental and numerical investigations on the synergistic effect of plasma nitriding and notch size on the fatigue properties of AISI 4140 steel

Engineering structures across various sectors frequently experience fatigue damage under operational conditions, which significantly reduces their operational lifespan. Moreover, fatigue strength of the materials reduces when they have geometries such as notches and sharp corners because they constitute stress concentrations. On the other hand, different surface treatments can efficiently increase in managing the lifetime and performance of materials. In the current study, the fatigue properties of untreated and plasma nitrided notched steel samples were compared through numerical analyses and fatigue experiments. For this investigation, fatigue test specimens with different notch sizes made out of AISI 4140 steel were plasma nitrided at 460 degrees C and 535 degrees C for 9 h in a glow discharge environment. The specimens were analysed using XRD, SEM, and microhardness tester to ascertain their structural, morphological, and mechanical characterization. The notch fatigue behaviour of nitride samples was analysed numerically by the Finite Element Analysis (FEA). Furthermore, a rotational bending fatigue test system was utilized to conduct fatigue tests and consequently, fatigue date obtained from experimental results and FEA were compared. It was found that the thicknesses of compound layer and diffusion zone, compressive residual stresses, and hardness enhanced as the process temperature increased. Additionally, an increase of by up to 110 % was obtained in the notch fatigue resistance of the specimens under constant amplitude loading. According to the results obtained, it was observed that there were acceptable errors between the experimentally obtained values and the values obtained from the FEA. The results show that in all plasma nitrided notched samples, the fatigue crack initiation shifted towards the core and thus the fatigue strength increased, and especially at the increasing plasma nitriding process temperature, the R4 and R8 notch geometries exhibited better fatigue performance improvement than the other samples.

Dergi

THEORETICAL AND APPLIED FRACTURE MECHANICS

Yıl

2025

Cilt

137

ISSN

0167-8442

eISSN

1872-7638

DOI

10.1016/j.tafmec.2025.104864

WoS UID

WOS:001425729200001