Long-term stable and high responsivity visible-ultraviolet photodetector of Se-doped CdO film on Si by spin coating
Sakar, Betul Ceviz, Orhan, Zeynep, Yildirim, Fatma, Aydogan, S.
Se-doped CdO thin films were prepared on p-Si substrates via spin coating. Morphological, structural and absorption measurements of CdO:Se film was performed. Then, a CdS:Se/p-Si heterojunction was produced by coating CdO:Se film on a p-Si substrate using spin coating method. From the I-V measurements, it has been seen that the device has a very good rectification feature in the dark, at room temperature. In order to investigate the performance of the device under light, a detailed analysis was performed by performing I-V measurements under ultraviolet (UV) light (365 and 395 nm, 10 mW cm(-2)) and different intensities of visible light (between 10 and 125 mW cm(-2)) as well as ambient light. It was observed that the CdO:Se/p-Si heterojunction performed well under both illumination conditions. The maximum responsivity and specific detectivity values were obtained as 0.72 and 4.47 A W-1 and 3.31 x 10(9) and 2.05 x 10(10) Jones for visible and UV regions, respectively. It was also seen that the device exhibited very high performance and stability even after 160 days.
- Dergi
- JOURNAL OF PHYSICS D-APPLIED PHYSICS
- Yıl
- 2023
- Cilt
- 56
- Sayı
- 34
- ISSN
- 0022-3727
- eISSN
- 1361-6463
- DOI
- 10.1088/1361-6463/acd461
- WoS UID
- WOS:000990367400001